Magnetic Properties of Fe49Co33Ni18Nanowire ArraysStudied by First-Order Reversal Curve Diagrams مقاله

نویسنده مسئول:

نویسنده:

علمی-پژوهشی (وزارت علوم) (10 صفحه - از 449 تا 458)

چکیده:

Fe<sub>49</sub>Co<sub>33</sub>Ni<sub>18</sub> nanowire arrays (175 nm in diameter and lengths ranging from 5 to 32μm) were fabricated into nanopores of hard-anodized aluminum oxide templates using pulsed ac electrodeposition technique. Hysteresis loop measurements indicated that increasing the length decreases coercivity and squareness values (from 274 Oe and 0.58 to200 Oe and 0.105, respectively), indicating the increase in magnetostatic interactions between the nanowires (NWs).On the other hand, first-order reversal curve measurements showed a linear correlation between the magnetostatic interactions and length of NWs. It was also found that with increasing length, the domain structure of NWs changed from single-domain to pseudo single-domain state. A multidomain-like behavior is also seen for the longest NWs length.Increasing the length of NWs resulted in an increase inthe interaction and decrease in the array coercive field as beingsmaller than that of individual NWs (.The observed CFD component in the FORC diagrams of FeCoNi NWs with shorter lengths was a consequence ofnon-uniform length distributions.

کلیدواژه ها:

Pulsed ac electrodeposition ، Magnetostatic interactions ، FeCoNi nanowires ، FORC diagrams


برای مشاهده محتوای مقاله لازم است ورود پایگاه شوید. در صورتی که عضو نیستید از قسمت عضویت اقدام فرمایید.

لمشاهدة محتوی المقال یلزم الدخول إلی دخول الموقع.
إن كنت لا تقدر علی شراء الاشتراك عبرPayPal أو بطاقة VISA، الرجاء ارسال رقم هاتفك المحمول إلی مدير الموقع عبر credit@noormags.ir.

You should become a Sign in to be able to see articles.
If you fail to purchase subscription via PayPal or VISA Card, please send your mobile number to the Website Administrator via credit@noormags.ir.